A pipe in a spacecraft, made of AISI 310 stainless steel, is near the rocket engine, causing it to be subjected to temperatures as high as 950°C. The stress applied to the pipe in actual service is expected to be 10 MPa. (a) How long would you allow the pipe to be subjected to the given temperature and stress if a safety factor of 10 on life is required? (b) What safety factor on stress is achieved by the safety factor of 10 on life? Does the resulting safety factor on stress seem reasonable and adequate?

A pipe in a spacecraft, made of AISI 310 stainless steel, is near the rocket engine, causing it to be subjected to temperatures as high as 950°C. The stress applied to the pipe in actual service is expected to be 10 MPa. (a) How long would you allow the pipe to be subjected to the given temperature and stress if a safety factor of 10 on life is required? (b) What safety factor on stress is achieved by the safety factor of 10 on life? Does the resulting safety factor on stress seem reasonable and adequate?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Scanned by CamScanner EXAMPLE 1.39. A composite bar made up of aluminium and steel is held between two supports as shown in Fig. 1.55. The bars are stress free at the tcmperature of 38 C. What will be the stresses in the when the 21°C if, (a) the supports are unyielding, and (b) the supports each other by 0.1 mm. li can be assumed that the change of temperature is uniform all along the length of the bar, E for steel= 2.1x 10 kg/cm", E for alu- minium-7.4x 105 kg/cm2, coefficient of expansion for steel a,=11.7 two bars temperatnre is Steel bar dia. 50 mm Aluminium bar dia. 25 mm come пеarer to 60 cm- -30 cm- Fig. 1.55 x 10 per °C; aA for aluminium=23.4 x 10' per °C. (4.M.I.E.)
Suppose that you are making preliminary design calculations for a deep submersible vehicle that is to have a cylindrical hull with hemispherical ends and a 1.5-m radius. At its operating depth, the internal pressure will be 1E5 Pa, and the external pressure will be 330E5 Pa. Choose an aluminum alloy from Appendix B (recommend to use 2014-T6 aluminum alloy the normal yield stress is 410 MPa), and determine the necessary thickness of the hull so that it has a safety factor FS = 2.
Sketch a tensile member with (a) a rectangular crosssection, (b) a solid circular cross section, and (c) a circulartubecross section, and label the dimensions symbolically (e.g.,label the radius for the solid circular case). For each member, write out the definition of engineering stress in terms of the actual dimensions of the component. If therectangular member has dimensions of width and thicknessequal to 1 cm 0.3 cm, what would be the radius of a solidcircular member such that the stress is equal for an equaltensile load? If a tube has an outer radius equal to that ofthis same solid cylinder, what is the maximum inner radiussuch that the stress does not exceed 200% of the stress inthe solid cylinder?
A compressed gas cylinder for use in mechanical engineering laboratory has an internal gage pressure of 8 MPa at the time of delivery. The outside diameter of the cylinder is 30 cm. If the steel has an allowable stress of go MPa, what is the required thickness of the wall in centimeter? Is it considered a thin walled? [Checking: thickness/inside radius < o.1, thin walled) "Yes or No Next pa IS ACTIVITY Quiz 1 NEXT ACTIVITY Midterm Exam Jump to.. Learning Management System initiative from UCU-MiS+ based on moodle platform. ere to search 72 HUAWEI
An aluminum specimen subjected to the Brinell hardness test, the indenter and indentation diameters are 14 mm & 4.22 mm respectively. Determine the surface area of indentation, Also, determine the force applied on the aluminum specimen, if Brinell hardness value is 667. Solution: 1. The surface area of Indentation in mm2 is 2. The force applied in N is
Given is a thin-walled tube with the following data: Wall thickness- 2mmABC is a sector with a radius of 50 mmAOD & COD is a triangleTorque is 1000 N.mLength of the thin walled tube is 0.5 mUse G=24 GPa for aluminium Determine the following:a. Enclosed Areab. Perimeter of the thin walled tubec. Shear flowd. Shear stresse. Angle of twist
M13.6 Principal stresses from rosette data scenes -200 µE 23 Eb = 200 με Ec 500 µE 30° 30° Ex (LE) a Ey (µE) Yxy (Lurad) The strain rosette shown was used to obtain normal strain data at a point on the free surface of a steel (E = 200 GPa; v = 0.32) plate. Op1 (MPa) Determine the normal strains, the shear strain, and the principal stresses in the x-y plane. Op2 (MPa) Try One 1st 2nd 3rd attempt enter
Show complete solution pls A steel pipe has an inside diameter of d = 250 mm and an outside diameter of D = 268 mm. The length of the pipe is L = 6.0 m. Thechanges in dimension caused by an increase in temperature of 80°C for the:1. Outside diameter 2. Inside diameter 3. LengthNote: All answer must be round off up to 3 decimal places.
View Policies Current Attempt in Progress At a point on the free surface of a stressed body, a normal stress magnitude of S,- 73 MPa (T) and an unknown negative shear stress exist on a horizontal plane. Ome principal stress at the point is 187 MPa (T). The maximum in-plane shear stress at the point has a magnitude of 86 MPa. Determine the unknowVn stresses on the vertical plane, the unknown principal stress, and the absolute maximum shear stress at the point. Answers: MPa o, = MPa TIy = MPa O2 = MPa Toe max 1:29 31°C A
Question 1 A copper tube that experience a temperature change is placed between two rigid caps. Four steel bolts are symmetrically arranged parallel to the axis of the tube and are lightly fastened. The copper has a cross-sectional area, length, Young's modulus and coefficient of expansion of 2000 mm², 300 mm, 100 GPa and 16 x 10-6 /°C respectively. The steel has a diameter, Young's modulus and coefficient of expansi on of 22 mm, 200 GPa and 12 x 10-6/°C respectively. Find the stress in the tube if the temperature of the assembly is raised by 70°C 1.1 1.2 What load will each bolt carry at the raised temperature
4 In hardness test, a force of 3000 kgf applied using steel ball of 10 mm, the result hardness value is (BHN=200+N) where N is your number in class. Calculate the mean depression w bli nöy :diameters (d)? N=92
A steel bar of 8 mm is heated from 10° C to 25° Cand the bar is free to expand. The bar will induce Tensile stress No stress Compressive stress Shear stress